[1]杨睿①,王正宏②,王伯良①,等.含铝固液混合燃料老化性能研究[J].爆破器材,2016,45(01):34-38.[doi:10.3969/j.issn.1001-8352.2016.01.008]
 YANG Rui,WANG Zhenghong,WANG Boliang,et al.Aging Properties of Solidliquid Mixed Fuels Containing Aluminum[J].EXPLOSIVE MATERIALS,2016,45(01):34-38.[doi:10.3969/j.issn.1001-8352.2016.01.008]
点击复制

含铝固液混合燃料老化性能研究()
分享到:

《爆破器材》[ISSN:1001-8352/CN:32-1163/TJ]

卷:
45
期数:
2016年01
页码:
34-38
栏目:
爆炸材料
出版日期:
2016-01-29

文章信息/Info

Title:
Aging Properties of Solidliquid Mixed Fuels Containing Aluminum
文章编号:
5031
作者:
杨睿王正宏王伯良田少康程宇腾李世伟
①南京理工大学化工学院(江苏南京,210094)
②辽宁庆阳特种化工有限公司(辽宁辽阳,111002)
Author(s):
YANG Rui WANG ZhenghongWANG Boliang TIAN Shaokang CHENG Yuteng LI Shiwei
①School of Chemical Engineering, Nanjing University of Science and Technology (Jiangsu Nanjing, 210094)
②Qingyang Chemical Industry Corporation (Liaoling Liaoyang,111002)
关键词:
固液混合燃料老化性能加速老化试验
Keywords:
solid-liquid mixed fuels aging properties accelerated aging test
分类号:
TQ564;TJ55
DOI:
10.3969/j.issn.1001-8352.2016.01.008
文献标志码:
A
摘要:
为了研究某含铝固液混合燃料的老化性能,采用71 ℃高温加速老化试验方法,对燃料老化前后的燃烧热、机械感度、结构形貌及安定性进行了对比。结果表明,该含铝固液混合燃料在71 ℃下储存28 d后,燃烧热下降了0.86 %;摩擦感度从8 %下降到5 %,撞击感度无变化;混合燃料的间隙略有减小,但整体黏结结构并未被破坏;加热速率趋于0时的起始分解温度和峰值温度比老化前分别提前了7.1 ℃和1.6 ℃,活化能降低10.4 kJ/mol。与老化前相比,老化后燃料的各性能变化幅度较小,仍然满足燃料的使用要求,具有较好的长期储存性。
Abstract:
The accelerated aging tests at 71℃ were carried out in order to investigate the aging performance of a kind of solidliquid mixed fuel containing aluminum. Heat of combustion, mechanical sensitivity, micro structure and thermal stability were measured before and after aging. Results show that after 28day aging test at 71 ℃, the heat of combustion decreases by 0.86%, the friction sensitivity decays from 8% to 5%, while the impact sensitivity does not change. The gaps of the fuel become slightly smaller, but the overall bonding structure is not damaged. When the heating rate tends to zero the decomposition initial temperature and peak temperature shift by 7.1 ℃ and 1.6 ℃ downwards, respectively. The apparent activation energy reduces by 10.4 kJ/mol. In comparison with the fuel before aging, the performance of the aged fuel has little change and remains a good storage performance, still meeting the requirement.

参考文献/References:

[1]姚金侠,胥会祥,于海江,等. 燃料空气炸药的发展现状及展望[J].飞航导弹, 2014(2): 85-89.
[2]罗天元,周堃,余淑华,等.国外弹药贮存寿命试验与评价技术概述[J].装备环境工程,2005, 2(4): 17-22.
 LUO T Y, ZHOU K, YU S H, et al. Summarization on foreign ammunition storage life test and evaluation technology[J]. Equipment Environmental Engineering,2005,2(4):17-22.
[3]丁黎,郑朝民,梁忆,等.RDX基浇铸PBX的老化性能[J].含能材料,2015,23(2):156-162. DING L, ZHENG C M, LIANG Y, et al. Aging properties of casted RDXbased PBX[J]. Chinese Journal of Energetic Materials,2015,23(2):156-162.
[4]HOFFMAN D.M. Dynamic mechanical signatures of aged LX-17-1 plastic bonded explosive[J]. Journal of Energetic Materials, 2001, 19(2/3): 163-193.
[5]KADIRESH P N, SRIDHAR B T N. Experimental study on ballistic behaviour of an aluminised AP/HTPB propellant during accelerated aging[J]. Journal of Thermal Analysis and Calorimetry, 2010, 100(1): 331-335.
[6]CERRI S, BOHN M A, MENKE K, et al. Aging of HTPB/Al/AP rocket propellant formulation investigated by DMA measurements[J]. Propellants, Explosives, Pyrotechnics, 2013, 38 (2): 190-198.
[7]白春华,梁慧敏,李建平,等.云雾爆轰[M].北京:科学出版社,2012:17-50.
[8]张奇,闫华,白春华,等. 固液混合燃料物理稳定性分析[J].火炸药学报,2003,26(4):47-50.
ZHANG Q, YAN H, BAI C H. et al. Analysis on the physical stability of the solidliquid mixed fuel[J].Chinese Journal of Explosives & Propellants, 2003,26(4):47-50.
[9]段云,张奇,向聪,等. 固液混合装药热传导特性对其安全性影响的计算研究[J].高压物理学报,2010,24(3):181-186.
DUAN Y, ZHANG Q, XIANG C, et al. A calculation study on the effect of the heat conduction on the safety of the solidliquid mixed charge[J]. Chinese Journal of High Pressure Physics,2010,24(3):181-186.
[10]董海山,周芬芬. 高能炸药及相关物性能[M]. 北京:科学出版社, 1989.
[11]胡庆贤,吕子剑. TATB、石蜡、石墨钝感作用的讨论[J]. 含能材料, 2004, 12(1): 26-29.
 HU Q X, LU Z J. Study on desensitizing effect of TATB, wax and graphite[J]. Chinese Journal of Energetic Materials,2004,12(1):26-29.
[12]汤崭,杨利, 乔小晶,等. HMX热分解动力学与热安全性研究[J]. 含能材料, 2011, 19(4): 396-400.
 TANG Z, YANG L, QIAO X J, et al. On thermal decomposition kinetics and thermal safety of HMX[J]. Chinese Journal of Energetic Materials, 2011, 19(4): 396-400
[13]郑亚峰,南海,席鹏,等.不同比例AlRDX混合炸药的热分解活化能研究[J]. 爆破器材,2015,44(5):13-17.
ZHENG Y F, NAN H, XI P, et al. Research of thermal decomposition activation energy on AlRDX hybrid explosives with different components ratio[J]. Explosive Materials, 2015,44(5):13-17.

备注/Memo

备注/Memo:
收稿日期:2015-10-17
作者简介:杨睿(1991~),女,硕士,主要从事含能材料性能研究。E-mail:yangrui_1008@126.com
通信作者:王伯良(1964~ ),男,教授,主要从事爆炸力学的研究。E-mail:boliangwang@163.com
更新日期/Last Update: 2016-01-28