JO-6炸药耐热性试验研究()
分享到：

《爆破器材》[ISSN:1001-8352/CN:32-1163/TJ]

卷:
41
期数:
2012年03
页码:
1-3、7
栏目:
基础理论
出版日期:
2012-06-20

文章信息/Info

Title:
Experimental Study on Heat-resistance Property of JO-6 Explosive
文章编号:
4444
作者:
冯晓军 王晓峰 田轩 黄亚峰 赵东奎
西安近代化学研究所（陕西西安，710065）
Author(s):
FENG Xiaojun;  WANG Xiaofeng;  TIAN Xuan;  HUANG Yafeng;  ZHAO Dongkui
Xi’an Modern Chemistry Research Institute (Shanxi Xi’an, 710065)
关键词:
JO-6炸药; 耐热性能; 热爆炸; 转晶
Keywords:
JO-6 explosive;  heat-resistance property;  thermal explosion;  polymorphic transformation
分类号:
TJ55 TD235.2+1
文献标志码:
A
摘要:
为了研究JO-6炸药柱的耐热性能，利用自行研制的热爆炸试验系统进行了JO-6炸药柱的全历程试验和180℃条件下的热终止试验。探讨了装药状态对JO-6炸药热爆炸反应温度的影响，分析了有约束和无约束两种条件下HMX转晶对JO-6炸药柱结构和尺寸的影响。结果表明，粉态装药的热爆炸反应温度高于柱态装药，但对晶型转变温度没有明显影响，随着加热温度的升高，两种装药状态下的JO-6炸药均在180℃会发生HMX的转晶吸热，同时引起试样整体结构的破坏，使得试样尺寸增大，密度减小，试样在无约束条件下的结构破坏要大于有约束条件。
Abstract:
In order to investigate the heat-resistance properties of JO-6 explosive, a temperature ramp test and an isothermal test at 180℃ were carried out using the selfconstructed thermal explosion test system. The influence of the charge state on the thermal explosion temperature of JO-6 explosive was discussed and the influence of polymorphic transformation of HMX in both confined and unconfined conditions on its structure and dimension were analyzed. The results show that the thermal explosion temperature of powdery explosive is higher than that of cylindrical charge, while the charge state has no influence on polymorphic transformation temperature. With the temperature increasing, the occurrence of decalescence at 180℃ during the polymorphic transformation of HMX in JO-6 explosive, despite the two charge states, leads to the destruction of the sample, resulting in increasing in dimension and decreasing in density. The sample destruction of unconfined was more serious than that of confined condition.

参考文献/References:

［1］李晋庆. 几种新型石油射孔弹的研究和讨论［J］. 爆破器材,2003,32(4)：27-30.
［2］孙国祥,王晓峰,孙富根,等. 油气井射孔器用炸药及其安全性［J］. 爆破器材,2002,31(2)：4-9.
［3］赵捍东,张会锁,王芳,等. 不同炸药对聚能射流影响的数值模拟［J］. 弹箭与制导学报,2006(S1)：229-331.
［4］孙国祥. H781炸药研究报告［R］. 二○四所档案馆,1996.
［5］石健. 无杵堵射孔弹的研制［J］. 爆破器材, 1998,27(1)：30-32.
［6］赵省向. JO-6炸药热安全性研究［R］. 二○四所档案馆,1995.
［7］冯晓军.火炸药柱热爆炸试验系统研制报告［R］. 二○四所档案馆,2006.
［8］刘子如.含能材料热分析［M］.北京：国防工业出版社,2008.
［9］董海山,周芬芬.高能炸药及相关物性能［M］.北京：科学出版社,1989.
［10］兵器工业第二○四研究所.火炸药手册（第四分册）［M］.1987.

备注/Memo

备注/Memo:
收稿日期：2011-12-30
基金项目：国防火炸药基础科研专项。
作者简介：冯晓军（1976~），男，博士，高级工程师，主要从事炸药生产评估技术研究。
更新日期/Last Update: 2012-06-21